Alumina Grinding Beads 92%
High-density and low wear loss 92% alumina grinding beads, widely used in Zirconia, chemical, oil, enamel, pigment, mine, etc.
1) Al2O3: 92%2) Density: 3.6g/cm³3) EWT: <0.01%4) Compressive strength: above 2,000MPa5) Water absorption: <0.016) Crushing strength:...
Alumina Grinding Beads 92%
High-density and low wear loss 92% alumina grinding beads, widely used in Zirconia, chemical, oil, enamel, pigment, mine, etc.
Alumina Grinding Beads 92%1) Al2O3: 92%2) Density: 3.6g/cm³3) EWT: <0.01%4) Compressive strength: above 2,000MPa5) Water absorption: <0.016)...
92% Alumina Lining Bricks
92% Alumina Lining Bricks
1.groove design to optimize liner life
2.Water absorption: <0.01
92% Alumina Lining Bricks,Alumina balls,ceramic balls1) Al2O3: 92%2) Density: 3.6g/cm³3) Compressive strength: above 2,000MPa4) Water absorption: <0.015) Crushing strength:...
High Alumina Lining Bricks
High-density and low wear loss alumina lining bricks, widely used in ceramics, glass, porcelain, enamel, pigment, mine, etc.
alumina lining bricks1) Al2O3: 92%2) Density: 3.6g/cm³3) Compressive strength: above 2,000MPa4) Water absorption: <0.015) Crushing strength:...
Alumina Grinding Cylinders (Rod Shapes)
High-density and low wear loss alumina grinding cylinders (rod shapes), used in mine industries
1) Al2O3: 92%2) Density: 3.6g/cm³3) Compressive strength: above 2,000MPa4) Water absorption: <0.015) Crushing strength: ≥520kN6) Hardness: 9 (Mohs) 7) Size: 12mm, 20mm,...
High Alumina Lining Bricks
High-density and low wear loss alumina lining bricks, widely used in ceramics, glass, porcelain, enamel, pigment, mine, etc.
alumina lining bricks1) Al2O3: 92%2) Density: 3.6g/cm³3) Compressive strength: above 2,000MPa4) Water absorption: <0.015) Crushing strength:...
High Alumina Balls
High-density and low wear loss high alumina balls, widely used in ceramics, glass, porcelain, enamel, pigment, mine, etc.
High alumina balls for grinding1) Al2O3: 92%2) Density: 3.60g/cm³3) EWT: <0.01%4) Compressive strength: above 2,000MPa5) Water absorption:...
Alumina Balls 92%
High-density and low wear loss 92% alumina balls, widely used in ceramics, glass, porcelain, enamel, pigment, mine, etc.
92% alumina balls for grinding1) Al2O3: 92%2) Density: 3.60g/cm³3) EWT: <0.01%4) Compressive strength: above 2,000MPa5) Water absorption: <0.016)...
High Alumina Grinding Balls
High-density and low wear loss alumina balls, widely used in ceramics, glass, porcelain, enamel, pigment, mine, etc.
alumina grinding balls1) Al2O3: 92%2) Density: 3.6g/cm³3) EWT: <0.015%4) Compressive strength: above 2,000MPa5) Water absorption: <0.016) Crushing...
92% Alumina Balls
High-density and low wear loss 92% alumina balls, widely used in ceramics, glass, porcelain, enamel, pigment, mine, etc.
92% alumina balls for grinding1) Al2O3: 92%2) Density: 3.60g/cm³3) EWT: <0.01%4) Compressive strength: above 2,000MPa5) Water absorption: <0.016)...